Kramp White Primer 1L

Reference TB-222208KR

Etat: Nouveau

Tell us if you find an item cheaper elsewhere and we will do our best to beat the price

By buying this product you can collect up to 2 points . Your cart will total 2 points that can be converted into a voucher of €0.40 .

Specifications	- Can also be applied as a thick layer - Quick drying - Active corrosion protection (zinc phosphate)
Benefits	- High coverage - Saves time - Ensures a long service life
Application	- Suitable for iron and steel
Properties	- Can be coated with 1K and 2K varnishes - Base coat: Kramp primer (coat thickness: 50–60 µm) - Can be stored outside for up to 5 days without a final coating layer - High filling capability - For electrostatic processing - Temperature resistance: continuous load 120°C, transient load 150°C - Dry matter content: 65–70% - Basic viscosity (DIN 53 211): thixotropic - Specific weight (DIN 51 757): 1.4–1.5 kg/l - Gloss (DIN 67 530): 10–20%/60° (matt) - Chromate-free and lead-free - Adhesion (DIN 53 151): iron, steel: class 0 (very good)
Technical information	- Processing conditions: from +10°C and up to 80% relative humidity - Surface preparation: The object to be treated must be thoroughly cleaned, degreased and sanded as necessary - Dust-dry after 15–20 minutes (at 20°C) - Set to touch after 45–60 minutes (at 20°C) - Set to touch after 4–5 hours (at 20°C) - Final hardness after 3–4 days (at 20°C) - Using Kramp rapid drying hardener can reduce drying times - Lower temperatures result in longer drying times
Base colour	White
Base	Synthetic resin